Tungsten(VI) oxide supported rhodium nanoparticles: Highly active catalysts in hydrogen generation from ammonia borane

Herein, we report the use of tungsten(VI) oxide (WO₃) as support for Rh⁰ nanoparticles. The resulting Rh⁰/WO₃ nanoparticles are highly active and stable catalysts in H₂ generation from the hydrolysis of ammonia borane (AB). We present the results of our investigation on the particle size distribution, catalytic activity and stability of Rh⁰/WO₃ catalysts with 0.5%, 1.0%, 2.0% wt. Rh loadings in the hydrolysis reaction. The results reveal that Rh⁰/WO₃ (0.5% wt. Rh) is very promising catalyst providing a turnover frequency of 749 min^?1 in releasing 3.0 equivalent H₂ per mole of AB from the hydrolysis at 25.0 °C. The high catalytic activity of Rh⁰/WO₃ catalyst is attributed to the reducible nature of support. The report covers the results of kinetics study as well as comparative investigation of activity, recyclability, and reusability of colloidal(0) nanoparticles and Rh⁰/WO₃ (0.5 % wt. Rh) catalyst in the hydrolysis reaction.     

Characteristics of polycarbosilanes produced under different synthetic conditions and their influence on SiC fibers: Part I

SiC fibers can be obtained by the spinning, curing, and heat treatment of polycarbosilane (PCS); however, the properties of the PCS precursor must be considered to set the correct spinning conditions. Although many studies have focused on the synthesis conditions, the characterization (in particular, the structural characteristics) of PCS fibers, and the polymer itself has limitations. In this study, PCS was prepared in two steps, and the growth of the polymer with respect to the reaction conditions was analyzed. We found that PCS is formed and grown by the rearrangement and subsequent condensation reactions of polydimethylsilane (PDMS). Further, fiber formation was affected by the reaction temperature, time, and pressure. Three types of PCS were obtained under different synthetic conditions, and they were all characterized. Regardless of the structural similarity of the PCS fibers (based on the spectroscopic analysis), the polymers showed different thermal and rheological properties. Our findings will be important in improving the production of PCS fibers (and subsequent SiC fibers) with finely controlled properties.     

High resistivity measurement of SiC wafers using different techniques

To establish fast, nondestructive, and inexpensive methods for resistivity measurements of SiC wafers, different resistivity-measurement techniques were tested for characterization of semi-insulating SiC wafers, namely, the four-point probe method with removable graphite contacts, the van der Pauw method with annealed metal and diffused contacts, the current-voltage (I-V) technique, and the contactless resistivity-measurement method. Comparison of different techniques is presented. The resistivity values of the semi-insulating SiC wafer measured using different techniques agree fairly well. As a result, application of removable graphite contacts is proposed for fast and nondestructive resistivity measurement of SiC wafers using the four-point probe method. High-temperature van der Pauw and room-temperature Hall characterization for the tested semi-insulating SiC wafer was also obtained and reported in this work.     

An integrated approach to the optimum utilization of national tungsten resources: Technology gaps

A critical review of the current status of tungsten resources, of state-of-the-art processing technology and of product development in India vis-a-vis the world scenario is presented. An attempt has been made to identify technology gap areas requiring attention.     

SiC（w）／TZP＋mullite陶瓷复合材料界面和组成设计与力学性能

本文从理论上分析了ＳｉＣ（ｗ）ＴＺＰ＋ｍｕｌｌｉｔｅ（ｐ）复合材料界面残余热应力及其在基质内的分布规律。提出在ＳｉＣ（ｗ）表面涂复Ａｌ２Ｏ３和在ＰＺＴ中加入ｍｕｌｌｉｔｅ（ｐ）联合作用来降低晶须／基质界面残余热应力的界面设计方案，导出ＳｉＣ（ｗ）和ｍｕｌｌｉｔｅ（ｐ）协同补强ＰＺＴ的匹配条件。制备了ＳｉＣ（ｗ）／ＴＺＰ＋ｍｕｌｌｉｔｅ（ｐ）复合材料并了ＳｉＣ（ｗ）表面涂层Ａｌ２Ｏ３厚度和ＳｉＣ（ｗ     

钨合金的各向异性及残余应力测试的可行性

Ｘ射线分析显示钨合金经旋锻后存在着择优取向性，据此探讨了残余应力测定的可能性，考察加工状态对不同晶面的应力常数和弹性模量的影响，实验表明选用ＣｏＫａ－（２２２）虽有织构干扰产生衍射强度的反常分布，但不破坏２θ与Ｓｉｎ＾２ψ的直线关系，仍适合应力测试。比较而言，选用ＦａＫａ－（３１０）可避免织构的影响。且因谱线尖锐，峰强度高更于实际测试，随着表面加工程度增加，半高宽值增大，应力常数值减小，弹性模量因     

废钢铁代用品

优质钢材的冶炼和高水平操作指标的获得需要优良的原料作保证。直接还原铁，碳化铁和脱碳粒铁作为废钢铁代用品，已显示出其价格和品质上的优越性，并弥补了废铁数量的不足，但因其各有自身的特点，故研究其理化性质和使用性能，将为大规模生产和使用创造必要的条件。     

氧化钨物理特征的测量

对铵钨青铜（ATB）、氢钨青铜（HTB），紫色氧化钨（TVO）和蓝色氧化钨（TBO）四种氧化钨粉的氮气吸附/脱附等温线数据的分析。可以得出其表面积，微孔体积，微孔分布，中孔体积，平均孔径和分数维数。吸附/脱附等温线数据的分析表明，TVO粉末具有最大的中孔体积，最小的微孔体积，最窄的孔径分布，最小的分数维数和最大的平均孔径，其有利于氢还原制取超细钨粉，而不利于掺杂工艺，HTB粉末具有最大的微孔体积，最宽的孔径分布，最高的分数维数和最小的平均孔径，对于掺杂工艺来说是有利的，ATB和ABO的上述参数界于TVO和HTB之间。结果表明，利用吸附/脱附等温线来研究氧化物的物理特征是一个很好的方法；在氧化钨用于氢还原工艺和掺杂工艺之前必须研究其物理特征。     

由制碱废渣制脱硫吸收剂配比优选的研究

文章探讨了由制碱废渣和电石渣混合制取脱硫吸收剂 ,不同混合比例对吸收剂的比表面积、脱硫能力的影响 ,从而确定最佳配比方案     

场激活加压燃烧合成WC-Ni复合材料的工艺参数研究

以钨、碳和镍为原料,在电场激活下,材料的燃烧合成和致密化同时进行,短时间内完成了碳化钨镍复合材料的制备。研究了场激活 加压燃烧合成中的工艺参数,如脉冲电流、能量控制模式、升温速率、最高温度和压力对反应的影响。测量了在反应合成和致密化前后的样品 收缩率。所制备的复合材料的相对密度,490N载荷下Vickers硬度和断裂韧性分别为99.2%,13.965GPa和5.9MP·m1/2。